Voltage switchable dielectric material having bonded particle constituents

ABSTRACT

A voltage switchable dielectric material comprising a concentration of multi-component particles that are individually formed by a mechanical or mechanochemical bonding process that bonds a semiconductive or conductive-type host particle with multiple insulative, conductive, or semi-conductive guest particles.

RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 12/356,490, filed Jan. 20, 2009, which claims benefit of priority to Provisional U.S. Patent Application No. 61/022,090, entitled PROCESS FOR MAKING VOLTAGE SWITCHABLE POLYMER COMPOSITE MATERIALS, filed Jan. 18, 2008; the aforementioned priority applications being incorporated by reference herein in their entireties.

FIELD OF ART

This application relates to compositions of voltage switchable dielectric material. More specifically, this application pertains to voltage switchable dielectric material having bonded particle constituents.

BACKGROUND

Voltage switchable dielectric (VSD) materials are known to be materials that are insulative at low voltages and conductive at higher voltages. These materials are typically composites comprising of conductive, semiconductive, and insulative particles in an insulative polymer matrix. These materials are used for transient protection of electronic devices, most notably electrostatic discharge protection (ESD) and electrical overstress (EOS). Generally, VSD material behaves as a dielectric, unless a characteristic voltage or voltage range is applied, in which case it behaves as a conductor. Various kinds of VSD material exist. Examples of voltage switchable dielectric materials are provided in references such as U.S. Pat. No. 4,977,357, U.S. Pat. No. 5,068,634, U.S. Pat. No. 5,099,380, U.S. Pat. No. 5,142,263, U.S. Pat. No. 5,189,387, U.S. Pat. No. 5,248,517, U.S. Pat. No. 5,807,509, WO 96/02924, and WO 97/26665, all of which are incorporated by reference herein.

VSD materials may be formed using various processes and materials or compositions. One conventional technique provides that a layer of polymer is filled with high levels of metal particles to very near the percolation threshold, typically more than 25% by volume. Semiconductor and/or insulator materials is then added to the mixture.

Another conventional technique provides for forming VSD material by mixing doped metal oxide powders, then sintering the powders to make particles with grain boundaries, and then adding the particles to a polymer matrix to above the percolation threshold.

Other techniques and compositions for forming VSD material are described in U.S. patent application Ser. No. 11/829,946, entitled VOLTAGE SWITCHABLE DIELECTRIC MATERIAL HAVING CONDUCTIVE OR SEMI-CONDUCTIVE ORGANIC MATERIAL; and U.S. patent application Ser. No. 11/829,948, entitled VOLTAGE SWITCHABLE DIELECTRIC MATERIAL HAVING HIGH ASPECT RATIO PARTICLES.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a process for forming VSD material using bonded particles, under an embodiment.

FIG. 2 illustrates a bonded particle 200 that may be formed using MCB techniques or systems, for use in composition of VSD material, according to an embodiment.

FIG. 3 illustrates a composition of VSD material that includes multi-component particles (formed by bonding processes), as described with previous embodiments.

FIG. 4A and FIG. 4B each illustrate different configurations for a substrate device that is configured with VSD material having a composition such as described with any of the embodiments provided herein.

FIG. 5 is a simplified diagram of an electronic device on which VSD material in accordance with embodiments described herein may be provided.

DETAILED DESCRIPTION

Embodiments described herein provide a voltage switchable dielectric material comprising a concentration of mufti-component particles that are individually formed by a mechanical or mechanochemical bonding process that bonds a conductive-type host particle with multiple insulative or semi-conductive guest particles.

As used herein, “voltage switchable material” or “VSD material” is any composition, or combination of compositions, that has a characteristic of being dielectric or non-conductive, unless a field or voltage is applied to the material that exceeds a characteristic level of the material, in which case the material becomes conductive. Thus, VSD material is a dielectric unless voltage (or field) exceeding the characteristic level (e.g. such as provided by ESD events) is applied to the material, in which case the VSD material is switched into a conductive state. VSD material can further be characterized as a nonlinear resistance material. In many applications, the characteristic voltage of VSD material ranges in values that exceed the operational voltage levels of the circuit or device several times over. Such voltage levels may be of the order of transient conditions, such as produced by electrostatic discharge, although embodiments may include use of planned electrical events. Furthermore, one or more embodiments provide that in the absence of the voltage exceeding the characteristic voltage, the material behaves similar to the binder (i.e. it is non-conductive or dielectric).

Still further, an embodiment provides that VSD material may be characterized as material comprising a binder mixed in part with conductor or semi-conductor particles. In the absence of voltage exceeding a characteristic voltage level, the material as a whole adapts the dielectric characteristic of the binder. With application of voltage exceeding the characteristic level, the material as a whole adapts conductive characteristics.

According to embodiments described herein, the constituents of VSD material may be uniformly mixed into a binder or polymer matrix. In one embodiment, the mixture is dispersed at nanoscale, meaning the particles that comprise the conductive/semi-conductive material are nano-scale in at least one dimension (e.g. cross-section) and a substantial number of the particles that comprise the overall dispersed quantity in the volume are individually separated (so as to not be agglomerated or compacted together).

Still further, an electronic device may be provided with VSD material in accordance with any of the embodiments described herein. Such electrical devices may include substrate devices, such as printed circuit boards, semiconductor packages, discrete devices, thin-film electronics, Light Emitting Diodes (LEDs), radio-frequency (RF) components, and display devices.

Embodiments described herein provide for use of nano and micro-sized particles as constituents of VSD material. In particular, nano and micro-sized particles may be bonded onto other conductive or semi-conductive particles, and the combined particles are distributed uniformly in a binder to form a VSD composition.

In one embodiment, the combined particles are distributed uniformly in a suitable binder at a concentration level that is at or just below the percolation threshold. In other embodiments, nano or micro-sized particles are selected for bonding with larger particles, so that the concentration of particles (conductor and semiconductor particles bonded with nano or micro sized semi-conductive or insulative particles) in the binder exceeds the percolation threshold. The percolation threshold may coincide with the concentration of particles needed to make the VSD material behave as a conductor at a relatively low voltage (substantially less than the clamp or trigger voltage). In many cases, the percolation threshold may coincide with a conductor or semiconductor particle concentration in range of 20-80% by volume (depending on physical characteristics of the particles, such as size).

As described herein, the bonded particles may individually include a conductor (or semi-conductor) that is bonded or coated with multiple nano/micro-sized particles. The nano/micro-sized particles may be uniformly distributed to coat the larger particles individually. The coated particles may also be uniformly distributed in the binder material. In an embodiment, the coated particles are distributed uniformly at nano-scale in the binder to form VSD material of desired electrical characteristics.

Embodiments recognize that micro and nano sized particles are difficult to uniformly distribute and use in the context described, as such particles usually exhibit strong cohesiveness (and an inherent tendency to aggregate), low flowability, and low stability. In order to facilitate use of nano and micro sized particles, embodiments employ techniques by which such small particles are directly bonded to a host particle, and the resulting combination is then uniformly distributed at nano-scale within a suitable matrix or binder to form VSD material.

FIG. 1 illustrates a process for forming VSD material using bonded particles, under an embodiment. In step 110, bonded particles are formed by combining relatively larger conductive or semi-conductive particles with smaller insulative or semiconductive micro or nano sized particiles. In an embodiment, MechanoChemical Bonding (MCB) techniques and systems are used in order to form bonded particles that have a direct and solid bond between (i) nano and micro-sized particles that are coated onto (ii) larger conductive or semi-conductive host particles. In general, MCB systems use mechanical energy, without binders, to create the direct and solid bonds. Variations to MCB bonding techniques may also be used, including plasma assisted MCB systems. In particular, the application of mechanical energy can be assisted with the use of plasma to clean the surface of the particles and enhance their “solid bonding”. MCB technology is different from ball milling or fluidized bed reactors because no fluid, milling media, or another other additives (other than the particles themselves) are required.

Step 120 provides that the bonded particles are uniformly dispersed at nano-scale in a suitable binder. A sonic agitator may uniformly mix the bonded particles into the binder.

Step 130 provides that the mixed binder composition is cured into a VSD composition. The binder may be applied on a target site in order to cure it into the desired VSD composition.

As described with an embodiment of FIG. 1, MCB systems and machines provide one technique by which conductor, semiconductor, and/or insulative particles to be coated on each other directly to form bonded particle constituents of VSD material. FIG. 2 illustrates a bonded multi-SHOK. component particle 200 that may be formed using MCB techniques or systems, for use in composition of VSD material, according to an embodiment. In one embodiment, a conductive core (or “host”) particle 210 is identified with suitable electrical properties. Suitable material for use as host particle 210 include, for example, nickel, aluminum, titanium, or stainless steel. The host particle 210 is coated with so-called “guest” particles 220 using MCB systems or techniques. The result is formation of particles that singularly comprise (i) a host particle, and (ii) one or more guest particles (i.e. mufti-component particle). Reference is made to Table 1, which lists combinations of suitable host material and guest material to form non-linear conductive particles. Such non-linear conductive particles may be distributed in a binder to form the VSD material that has desired electrical properties (such as clamping/trigger voltage).

In one implementation, guest particles 220 are insulative or semiconductive materials, as well as organic materials. As illustrated by Table 1, examples of insulative type material for guest particles 220 include silicon dioxide and aluminum oxide. Suitable conductive and/or semiconductive material for guest particles 220 may also include organic or inorganic materials, such as single or double-walled carbon nanotubes, graphenes, or carbon black. Various other combinations may also be provided.

Table 1 lists examples of conductive type host particles 210, coated with either semiconductive or insulative type guest particles 220 at varying thicknesses.

Host Material Guest Material Thickness Novamet Nickel INP400 or 4SP-10 Degussa P25 TiO2 10 wt % Guest Novamet Nickel INP400 or 4SP-10 Degussa P25 TiO2 20 wt % Guest Novamet Nickel INP400 or 4SP-10 Degussa R300 SiO2 10 wt % Guest Novamet Nickel INP400 or 4SP-10 Degussa R300 SiO2 20 wt % Guest Novamet Nickel INP400 or 4SP-10 PV Fast Red B 10 wt % Guest Novamet Nickel INP400 or 4SP-10 PV Fast Red B 20 wt % Guest HC Starck TiB2 Grade D Degussa P25 TiO2 10 wt % Guest HC Starck TiB2 Grade D Degussa P25 TiO2 20 wt % Guest HC Starck TiB2 Grade D Degussa R300 SiO2 10 wt % Guest HC Starck TiB2 Grade D Degussa R300 SiO2 20 wt % Guest HC Starck TiB2 Grade D PV Fast Red B 10 wt % Guest HC Starck TiB2 Grade D PV Fast Red B 20 wt % Guest

With specific reference to FIG. 2, a suitable conductive type host particle 210 is titanium diboride, and a suitable guest particle 220 may correspond to perylene (such as provided by PV FAST RED B from Clariant).

The singular particles formed from the combination of the host particles 210 and the guest particles 220 (as shown in FIG. 2) are collectively used to form VSD or non-linear resistive material, as described by a technique of FIG. 1 (and further illustrated by FIG. 3). The use of bonding techniques such as described above enable the formation of bonded particles as VSD constituents, without use of sintering. The ability to form such bonded particles without sintering enables better distribution of guest particles 220 about individual host particles 210. Additionally, in contrast to some conventional approaches for forming non-linear resistive materials using sintering processes, the use of MCB or similar techniques or processes does not damage heat-sensitive particles. For example, organic guest particles 220 may be used without concern that such particles would be damaged by heat.

While Table 1 lists several examples, numerous other combinations of materials may be used for both host particles 210 and guest particles 220. In one embodiment, the host particle 210 is conductive and of the order of 10-100 times larger in dimension than the guest particle 220. As another example, the host particle 210 corresponds to Nickel or Titanium Diboride, which are conductors that can have a diameter that ranges from 6 to 12 microns. In these examples, the host particle 210 may be coated with a 20-30 nanometer semiconductor (e.g. 26 nm perylene, which is organic, or nano-dimensioned titanium dioxide).

In another implementation, small or thin insulators (or semi-conductors) may be used for conductive purposes. Specifically, a conductive host particle 210 may be coated with small dimensioned insulators as the guest particles 220. Such small dimensional insulators may correspond to fumed Silica (7 nm dimensioned). As a thin insulator, conduction can occur using the thin insulator through quantum tunneling.

Table 2 lists examples of both host particles (first three rows) and guest particles (last three rows).

TABLE 2 Bulk “Apparent” d50 Vendor Material Grade Density Density (micron) HC Starck Titanium D 4.52 1 6 Diboride Accumet Titanium 4.52 1 12 Diboride Novamet Nickel 4SP-10 8.9 5.2 6.6 Degussa Titanium P25 3.93 0.13 0.021 Dioxide Degussa Fumed Silica R300 2.2 0.05 0.007 Clariant Perylene PV Fast 1.4 1 0.026 Red

In the examples of Table 2, the first 3 rows illustrate suitable Host particles, while the last 3 rows provide additional examples of Guest particles.

Thus numerous specific examples and embodiments are provided for herein, embodiments include coated particles for use in a composition of VSD material, where (i) the host particle 210 is a conductor or semiconductor (having micron(s) sized dimension); and (ii) the guest particle 220 is either conductor, semiconductor, or insulator that is nano or sub-micron sized.

More conductive host particles 210 can receive more guest particles 220, particularly organic material, which can ‘stick’ better or form better bonds with the host particle 210. However, in other embodiments, the host particle 210 is a semi-conductor, and the dimension of the Host particle as compared to the guest particle 220 may vary beyond the 10-100 ratio recited.

In one embodiment, the type of guest particle 220 used may also be conductive. Still further, the type of guest particle 220 may be both conductive and organic, thus providing enhanced bonding and additional conductivity.

Still further, an embodiment provides for additional coats or guest particles 220. Specifically, one or more embodiments provide for individual host particles 210 in the composition to be bonded with two or more types of guest particles 220. As an alternative or addition, the host particle 210 may be combined with an organic semiconductor particle.

With any of the embodiments described, the specific composition used may be varied depending on the electrical properties that are desired from the formed VSD or non-linear resistive material.

FIG. 3 illustrates a composition of VSD material that includes multi-component particles (formed by bonding processes), as described with previous embodiments. In an embodiment, a sample of VSD material 300 includes conductive particles (or host) 310, having guest material 320 formed through MCB bonding, and semiconductive particles 330. Some embodiments of VSD material include high aspect ratio (HAR) conductive or semiconductive fillers (“HAR particles 340”). Suitable HAR particles 340 include, for example, carbon nanotubes, nanorods, or nanowires.

As depicted in FIG. 3, the concentration of the particle constituents in the binder exceeds the percolation threshold. This means the particles, including the bonded mufti-component particles 310, are loaded into the binder 320 so that a particle path 350 is formed that extends across a thickness of the VSD material. The particle path 350 is signified by the particles being in contact with one another. Thus, when the particle concentration exceeds the percolation threshold, the formation of complete particle paths that extend the thickness of the VSD material is likely. In absence of guest material 330, the presence of the particle path 350 would likely render the composition conductive, so as to not have a dielectric state (i.e. VSD characteristics). The use of guest material 330, however, enables the semi- or non-conductive electrical properties of the guest material to provide a buffer that requires presence of field before the particle path is conductive. In this way, the guest material 330 can be selected to significantly influence the clamp or trigger voltage of the VSD material. Optionally semiconductive host materials may be coated with conductive guest materials and loaded to just below percolation.

As an addition or alternative to an embodiment such as depicted by FIG. 3, the composition of the VSD material may further comprise single-component conductor (or semi-conductor) particles. Thus, separate concentrations of conductor elements and mufti-component conductor elements (with guest material that may be insulative or semiconductive) may be used in some compositions of VSD material. Likewise, as depicted, separate concentrations of high aspect ratio nanoparticles may be dispersed in the VSD material (e.g. graphenes, carbon nanotubes, nanowires, nanorods, antimony in oxide (ATO) nanorods).

VSD Material Applications

Numerous applications exist for compositions of VSD material in accordance with any of the embodiments described herein. In particular, embodiments provide for VSD material to be provided on substrate devices, such as printed circuit boards, semiconductor packages, discrete devices, thin film electronics, as well as more specific applications such as LEDs and radio-frequency devices (e.g. RFID tags). Still further, other applications may provide for use of VSD material such as described herein with a liquid crystal display, organic light emissive display, electrochromic display, electrophoretic display, or back plane driver for such devices. The purpose for including the VSD material may be to enhance handling of transient and overvoltage conditions, such as may arise with ESD events. Another application for VSD material includes metal deposition, as described in U.S. Pat. No. 6,797,145 to L. Kosowsky (which is hereby incorporated by reference in its entirety).

FIG. 4A and FIG. 4B each illustrate different configurations for a substrate device that is configured with VSD material having a composition such as described with any of the embodiments provided herein. In FIG. 4A, the substrate device 400 corresponds to, for example, a printed circuit board. In such a configuration, VSD material 410 (having a composition such as described with any of the embodiments described herein) may be provided on a surface 402 to ground a connected element. As an alternative or variation, FIG. 4B illustrates a configuration in which the VSD material forms a grounding path that is embedded within a thickness 410 of the substrate.

Electroplating

In addition to inclusion of the VSD material on devices for handling, for example, ESD events, one or more embodiments contemplate use of VSD material (using compositions such as described with any of the embodiments herein) to form substrate devices, including trace elements on substrates, and interconnect elements such as vias. U.S. patent application Ser. No. 11/881,896, filed on Sep. Jul. 29, 2007, and which claims benefit of priority to U.S. Pat. No. 6,797,145 (both of which are incorporated herein by reference in their respective entirety) recites numerous techniques for electroplating substrates, vias and other devices using VSD material. Embodiments described herein enable use of VSD material, as described with any of the embodiments in this application.

Other Applications

FIG. 5 is a simplified diagram of an electronic device on which VSD material in accordance with embodiments described herein may be provided. FIG. 5 illustrates a device 500 including substrate 510, component 520, and optionally casing or housing 530. VSD material 505 (in accordance with any of the embodiments described) may be incorporated into any one or more of many locations, including at a location on a surface 502, underneath the surface 502 (such as under its trace elements or under component 520), or within a thickness of substrate 510. Alternatively, the VSD material may be incorporated into the casing 530. In each case, the VSD material 505 may be incorporated so as to couple with conductive elements, such as trace leads, when voltage exceeding the characteristic voltage is present. Thus, the VSD material 505 is a conductive element in the presence of a specific voltage condition.

With respect to any of the applications described herein, device 500 may be a display device. For example, component 520 may correspond to an LED that illuminates from the substrate 510. The positioning and configuration of the VSD material 505 on substrate 510 may be selective to accommodate the electrical leads, terminals (i.e. input or outputs) and other conductive elements that are provided with, used by or incorporated into the light-emitting device. As an alternative, the VSD material may be incorporated between the positive and negative leads of the LED device, apart from a substrate. Still further, one or more embodiments provide for use of organic LEDs, in which case VSD material may be provided, for example, underneath the OLED.

With regard to LEDs and other light emitting devices, any of the embodiments described in U.S. patent application Ser. No. 11/562,289 (which is incorporated by reference herein) may be implemented with VSD material such as described with other embodiments of this application.

Alternatively, the device 500 may correspond to a wireless communication device, such as a radio-frequency identification device. With regard to wireless communication devices such as radio-frequency identification devices (RFID) and wireless communication components, VSD material may protect the component 520 from, for example, overcharge or ESD events. In such cases, component 520 may correspond to a chip or wireless communication component of the device. Alternatively, the use of VSD material 505 may protect other components from charge that may be caused by the component 520. For example, component 520 may correspond to a battery, and the VSD material 505 may be provided as a trace element on a surface of the substrate 510 to protect against voltage conditions that arise from a battery event. Any composition of VSD material in accordance with embodiments described herein may be implemented for use as VSD material for device and device configurations described in U.S. patent application Ser. No. 11/562,222 (incorporated by reference herein), which describes numerous implementations of wireless communication devices which incorporate VSD material.

As an alternative or variation, the component 520 may correspond to, for example, a discrete semiconductor device. The VSD material 505 may be integrated with the component, or positioned to electrically couple to the component in the presence of a voltage that switches the material on.

Still further, device 500 may correspond to a packaged device, or alternatively, a semiconductor package for receiving a substrate component. VSD material 505 may be combined with the casing 530 prior to substrate 510 or component 520 being included in the device.

Embodiments described with reference to the drawings are considered illustrative, and Applicant's claims should not be limited to details of such illustrative embodiments. Various modifications and variations will may be included with embodiments described, including the combination of features described separately with different illustrative embodiments. Accordingly, it is intended that the scope of the invention be defined by the following claims. Furthermore, it is contemplated that a particular feature described either individually or as part of an embodiment can be combined with other individually described features, or parts of other embodiments, even if the other features and embodiments make no mentioned of the particular feature. 

1. A composition comprising: a binder; particles dispersed uniformly within the binder, wherein at least some of the particles are mufti-component particles that singularly comprise: a conductive-type host particle and multiple insulative or semi-conductive guest particles; wherein said composition is (i) dielectric in absence of a voltage that exceeds a characteristic voltage level, and (ii) conductive with application of said voltage that exceeds the characteristic voltage level.
 2. The composition of claim 1, wherein at least some of the particles singularly comprise the conductive host particle being bonded with the multiple insulative or semi-conductive guest particles through mechanical or mechano-chemical bonding.
 3. The composition of claim 1, wherein the particles are dispersed into the binder past a percolation threshold.
 4. The composition of claim 1, wherein the percolation threshold coincides with a conductor or semiconductor particle concentration in range of 20-80% by volume.
 5. The composition of claim 1, wherein the host particle is micron sized, and the guest particles are nano or sub-micron sized.
 6. The composition of claim 1, wherein the guest material is organic.
 7. The composition of claim 5, wherein the organic material corresponds to carbon nanotubes, perylene, or graphene.
 8. The composition of claim 1, wherein the guest material includes titanium dioxide or fumed silica.
 9. The composition of claim 1, wherein at least some of the particles are high-aspect ratio nanoparticles that are uniformly dispersed in the binder.
 10. The composition of claim 1, wherein the particles are dispersed into the binder past a percolation threshold, and wherein the characteristic voltage is dependent in part on a resistive characteristic of the guest material for the mufti-component particle.
 11. A voltage switchable dielectric material comprising a concentration of multi-component particles that are individually formed by a mechanical or mechanochemical bonding process that bonds a conductive-type host particle with multiple insulative or semi-conductive guest particles.
 12. The voltage switchable dielectric material of claim 11, wherein a particle concentration of the material exceeds percolation.
 13. The voltage switchable dielectric material of claim 11, further comprising: a concentration of single-component conductor elements in addition to the multi-component particles.
 14. The voltage switchable dielectric material of claim 11, further comprising: a concentration of high aspect ratio nano-particles.
 15. A device comprising: a layer of voltage switchable dielectric material provided as a protective layer against transient electrical conditions, wherein the voltage switchable dielectric material comprises a concentration of multi-component particles that are individually formed by a mechanical or mechanochemical bonding process that bonds a conductive-type host particle with multiple insulative or semi-conductive guest particles. 